Technology improvement for manufacturing and repair of collapsible pipelines
DOI:
https://doi.org/10.15587/2312-8372.2016.72931Keywords:
arc brazing, zinc coating, brazed seam, mechanical testing, joint strength, tensile forceAbstract
Application of arc brazing technology for manufacturing and repair of collapsible pipelines to replace arc MIG/MAG welding was proposed. The use of this technology to connect galvanized elements of collapsible pipelines preserving the protective coating in the joints was analyzed and justified.
Strength of samples of welded and brazed joints, galvanized pipes, collapsible field pipelines by tear test was investigated and strength characteristics of joints defined by measuring the hardness of a section connections was defined.
It was found that joints made by arc brazing by CuAl8 filler rod have the strength level of the welded joints. Due to the small thermal effects, with arc brazing, there is no destruction of the protective zinc coating at the joint place.
Research results allow recommending arc brazing technology by CuAl8 filler for manufacturing and repair of collapsible pipelines, preserving strength joints without destruction of the protective zinc coating at the joint place.
References
- Rozalski, M., Gawrysiuk, W. (2008, April). MIG/MAG braze-welding of galvanised steel sheets and examples of difficult to weld systems. Welding International, Vol. 22, № 4, 239–244. doi:10.1080/09507110802117693
- Miao, Y., Wu, B., Xu, X., Han, D. (2014, August 3). Effect of Heat Input on Microstructure and Mechanical Properties of Joints Made by Bypass-Current MIG Welding–Brazing of Magnesium Alloy to Galvanized Steel. Acta Metallurgica Sinica (English Letters), Vol. 27, № 6, 1038–1045. doi:10.1007/s40195-014-0118-3
- Makwana, P., Shome, M., Goecke, S.-F., De, A. (2016, May 18). Gas metal arc brazing of galvannealed steel sheets. Science and Technology of Welding and Joining, 1–7. doi:10.1080/13621718.2016.1145420
- Varol, F., Ekici, M., Ferik, E., Ozsarac, U., Aslanlar, S. (2015, April). Investigation of Mechanical Properties of MIG-Brazed TRIP 800 Steel Joints Using Different Working Angles. Acta Physica Polonica A, Vol. 127, № 4, 965–967. doi:10.12693/aphyspola.127.965
- Magda, A. V., Codrean, C. (2014, September). Corrosion Resistance Testing of the Galvanized Sheet Metal Braze Welding Joints. Key Engineering Materials, Vol. 627, 189–192. doi:10.4028/www.scientific.net/kem.627.189
- Magda, A., Popescu, M., Codrean, C., Mocuta, E. G. (2013, September). Possibilities of joining galvanized sheet steel using the CMT method (cold metal transfer). Welding International, Vol. 27, № 9, 665–667. doi:10.1080/09507116.2011.606137
- Tsumarev, Yu. A., Sheleg, V. K. (2010). Vliianie podgotovki kromok na povrezhdaemost' zashchitnogo pokrytiia pri dugovoi paike otsinkovanoi stali. Vestnik Polotskogo gosudarstvennogo universiteta, 2, 124–129.
- Rykała, J., Pfeifer, T. (2013, March 14). Influence of the technological conditions of welding using the MIG/MAG method on metal transfer in the welding arc. Welding International, Vol. 28, № 12, 931–940. doi:10.1080/09507116.2012.753233
- MIG/MAG istochniki pitaniia. FRONIUS UKRAINA. Available: http://www.fronius.com/cps/rde/xchg/SID-DD82EC17-570044F3/fronius_ukraine/hs.xsl/2510_2787.htm#.VqVBilkTBC1
- Stoev, P. I., Moshcheniuk, V. I. (2003). Opredelenie mehanicheskih svoistv metallov i splavov po tverdosti. Vestnik Kharkovskogo nauchnogo universiteta im. Karazina, 2, 106–112.
- Zvorykina, A. C., Strelenko, N. M. (2014). Features of the arc soldering of thin-sheet galvanized steel. Tehnologicheskie sistemy, 4, 42–45. Available: http://nbuv.gov.ua/UJRN/Ts_2014_4_6
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2016 Олег Михайлович Матвієнків
![Creative Commons License](http://i.creativecommons.org/l/by/4.0/88x31.png)
This work is licensed under a Creative Commons Attribution 4.0 International License.
The consolidation and conditions for the transfer of copyright (identification of authorship) is carried out in the License Agreement. In particular, the authors reserve the right to the authorship of their manuscript and transfer the first publication of this work to the journal under the terms of the Creative Commons CC BY license. At the same time, they have the right to conclude on their own additional agreements concerning the non-exclusive distribution of the work in the form in which it was published by this journal, but provided that the link to the first publication of the article in this journal is preserved.