Investigation of thermal stability, optical properties, phase and chemical composition of transparent conductive tin oxide films deposited by pyrolytic method on silica float glass
DOI:
https://doi.org/10.15587/2312-8372.2019.182863Keywords:
transparent conductive coatings, float glass, tin oxide doped with fluorine, thermal stabilityAbstract
The object of research is transparent conductive coating based on fluorine doped tin oxide deposited on silica float glass by the pyrolytic method. However, both in the manufacturing process of such a coating and in the process of its operation, degradation of its electrically conductive properties is observed. This may be due to changes in the structure of the coating under the influence of certain technological and operational factors, namely: process temperature, holding time, gas environment during the application and operation of a transparent electrically conductive coating. Studies have confirmed a significant increase in electrical conductivity. They also found a slight decrease in the transmittance of transparent oxide-tin films obtained with the introduction of ammonium fluoride as a dopant during the pyrolysis of 1M alcohol solutions of Sn2+ and Sn4+chlorides and are widely used as precursors for the content of such coatings. So, with a ratio of Sn4+/F=10 in working solutions, a minimum of specific surface resistance was fixed at 32 Ohm/m2. At the same time, a decrease in the value of the averaged transmittance in the optical wavelength range of 0.2-6.0 μm by 51 %, and in its visible part (0.4-0.8 μm) by 11 %. It is shown that thermal degradation of the coating is a significant factor in increasing the resistance values both in the technological process and during operational impacts. The results obtained indicate that reheating to temperatures above 450 °C leads to the appearance of the phenomenon of thermal degradation of the electrically conductive properties of the coating. So, during a 1-hour exposure at a temperature of 550 °C, the increase in specific surface resistance increases by 2 times and is fixed at 68 Ohm/m2 after complete cooling. Repeated heating cycles with the indicated parameters lead to a significantly lesser effect, which may indicate stabilization of the processes that occur during thermal destruction of the electrically conductive coating.
References
- Bach, H., Krause, D. (Eds.) (2003). Thin films on glass. Springer Science & Business Media, 436. doi: http://doi.org/10.1007/978-3-662-03475-0
- Minami, T. (2005). Transparent conducting oxide semiconductors for transparent electrodes. Semiconductor Science and Technology, 20 (4), S35–S44. doi: http://doi.org/10.1088/0268-1242/20/4/004
- Mattox, D. M. (2010). Handbook of physical vapor deposition (PVD) processing. William Andrew, 732. doi: http://doi.org/10.1016/c2009-0-18800-1
- Van Mol, A. M. B., Chae, Y., McDaniel, A. H., Allendorf, M. D. (2006). Chemical vapor deposition of tin oxide: Fundamentals and applications. Thin Solid Films, 502 (1-2), 72–78. doi: http://doi.org/10.1016/j.tsf.2005.07.247
- Lincot, D., Hodes, G. (2006). Chemical solution deposition of semiconducting and non-metallic films. The Electrochemical Society, 234.
- Wasa, K., Kanno, I., Kotera, H. (Eds.) (2012). Handbook of sputter deposition technology: fundamentals and applications for functional thin films, nano-materials and MEMS. William Andrew, 660.
- Manoj, P. K., Joseph, B., Vaidyan, V. K., Amma, D. S. D. (2007). Preparation and characterization of indium-doped tin oxide thin films. Ceramics International, 33 (2), 273–278. doi: http://doi.org/10.1016/j.ceramint.2005.09.016
- Elangovan, E., Ramamurthi, K. (2005). A study on low cost-high conducting fluorine and antimony-doped tin oxide thin films. Applied Surface Science, 249 (1-4), 183–196. doi: http://doi.org/10.1016/j.apsusc.2004.11.074
- Moholkar, A. V., Pawar, S. M., Rajpure, K. Y., Bhosale, C. H., Kim, J. H. (2009). Effect of fluorine doping on highly transparent conductive spray deposited nanocrystalline tin oxide thin films. Applied Surface Science, 255 (23), 9358–9364. doi: http://doi.org/10.1016/j.apsusc.2009.07.035
- Pavlushkin, N. M. (1983). Khimicheskaia tekhnologiia stekla i sitallov. Moscow: Stroiizdat, 432.
- Saito, K., Ikushima, A. J. (2002). Effects of fluorine on structure, structural relaxation, and absorption edge in silica glass. Journal of Applied Physics, 91 (8), 4886–4890. doi: http://doi.org/10.1063/1.1459102
- Li, J., Wang, L., Liu, J., Evmenenko, G., Dutta, P., Marks, T. J. (2008). Characterization of Transparent Conducting Oxide Surfaces Using Self-Assembled Electroactive Monolayers. Langmuir, 24 (11), 5755–5765. doi: http://doi.org/10.1021/la704038g
- Coutts, T. J., Young, D. L., Li, X. (2000). Characterization of Transparent Conducting Oxides. MRS Bulletin, 25 (8), 58–65. doi: http://doi.org/10.1557/mrs2000.152
- Gallagher, D., Scanlan, F., Houriet, R., Mathieu, H. J., Ring, T. A. (1993). Indium-tin oxide thin films by metal-organic decomposition. Journal of Materials Research, 8 (12), 3135–3144. doi: http://doi.org/10.1557/jmr.1993.3135
- Gordon, R. G. (1996). Preparation and properties of transparent conductors. MRS Online Proceedings Library Archive, 426. doi: http://doi.org/10.1557/proc-426-419
- Karthick, P., Vijayanarayanan, D., Sridharan, M., Sanjeeviraja, C., Jeyadheepan, K. (2017). Optimization of substrate temperature and characterization of tin oxide based transparent conducting thin films for application in dye-sensitized solar cells. Thin Solid Films, 631, 1–11. doi: http://doi.org/10.1016/j.tsf.2017.04.003
- Gnesin, G. G., Skorokhod, V. V. (Eds.) (2008). Neorganicheskoe materialovedenie. Enciklopedicheskoe izdanie v 2-kh tomakh. Kyiv: Naukova Dumka, 2900.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2019 Artem Iatsenko, Anastasiia Mishchenko, Boris Kornilovych
![Creative Commons License](http://i.creativecommons.org/l/by/4.0/88x31.png)
This work is licensed under a Creative Commons Attribution 4.0 International License.
The consolidation and conditions for the transfer of copyright (identification of authorship) is carried out in the License Agreement. In particular, the authors reserve the right to the authorship of their manuscript and transfer the first publication of this work to the journal under the terms of the Creative Commons CC BY license. At the same time, they have the right to conclude on their own additional agreements concerning the non-exclusive distribution of the work in the form in which it was published by this journal, but provided that the link to the first publication of the article in this journal is preserved.