Way to increase back-up rolls cracking and wearing resistances at high-speed deposition with low heat input
DOI:
https://doi.org/10.31498/2225-6733.34.2017.105584Keywords:
heat affected zone, cold and hot cracks, welding stresses, high-speed surfacing, low heat inputAbstract
The rolling-mill back-up rolls operate under high specific pressures conditions and are produced of high-carbon steel, prone to hot and cold cracking. Therefore crack resistance increase is an important scientific and technical problem. The impact of the electrode shape and heat input on the arc motion, and heat affected zone, the size of which determines the cold cracks formation and deposited metal flaking has been found. The arc moves along the electrode end face along the longitudinal axis or perpendicular to the weld pool in dependence on the ribbon position. The arc movement governs the heat input in the pool and if the surfacing regime is constant, the heating and cooling rates of the molten metal and heat affected zone as well. At surfacing with a perpendicular ribbon the heat affected zone decreases; at surfacing with a longitudinal ribbon and wire the heat affected zone increases. At surfacing with a composite electrode the heat affected zone reduces sharply while resistance to cracking and wearing increases. With the heat input reduction in weld pool side edges the heat affected zone reduces as well. At high speed surfacing with low heat input, the heat affected zone reduces, the tendency to cold cracking and deposited metal flaking decrease, welding stresses and specific pressure decrease, what results in resistance to cracking increase as well as the increase in wearing resistance. When energy decreases the deposited metal quality increases. Energy minimum results in maximum quality. The process of energy-saving high-speed deposition with low heat input, which provides microstructure reduction, heat input in the base metal and heat affected zone decrease, prevent cold cracking and deposited metal flaking increases both rolling mill back-up cracking resistance and wearing resistance has been developedReferences
Список использованных источников (ГОСТ):
Прохоров Н.Н. Физические процессы в металле при сварке / Н.Н. Прохоров. – Т. II. – М. : Металлургия, 1976. – 600 с.
Шоршоров М.Х. Фазовые превращения и изменения свойств стали при сварке / М.Х. Шоршоров, В.В. Белов. – М. : Наука, 1972. – 228 с.
Финкель В.М. Физика разрушения / В.М. Финкель. – М. : Металлургия, 1970. – 376 с.
Лысов В.С. Структура и стойкость против образования холодных трещин металла около шовной зоны стали 38ХС / В.С. Лысов, Т.А.Макарова, В.Г. Федоров // Сварочное производство. – 1982. – № 6. – С. 19-21.
Иванова Н.В. Хладостойкость металла ЗТВ сварных соединений резервуарных конструкций / Н.В. Иванова, В.Н. Дикун, В.А. Винокуров // Сварочное производство. – 1985. – № 11. – С. 15-17.
Влияние погонной энергии на образование отколов при наплавке высокоуглеродистой стали аустенитными проволоками / В.К. Каленскийи и др. // Автоматическая сварка. – 2001. – № 11. – С. 11-14.
Стеклов О.И. Стойкость наплавленного слоя против отслаивания в водородсодержащих средах / О.И. Стеклов, A.П. Алексеев, O.A. Александров // Сварочное производство. – 1989. – № 12. – С. 8-10.
Суслова Е.А. Влияние технологических факторов на склонность к образованию тре-щин / Е.А. Суслова, В.А. Игнатов, А.С. Зубченко // Сварочное производство. – 1990. – № 5. – С. 35-36.
Готальский Ю.Н. Способы сужения мартенситной прослойки в зоне сплавления перлитной стали с аустенитным швом / Ю.Н. Готальский, В.В. Снисарь, Д.П. Новикова // Сварочное производство. – 1981. – № 6. – С. 7-9.
References:
Prokhorov N.N. Fizicheskie processy v metalle pry svarke [Physical processes in the metal during welding]. Moscow, Metallurgija Publ., 1976. 600 p. (Rus.)
Shorshorov M.H., Belov V.V. Fazovije prevrashchenija e izmenenija svoystv staly pry svarke [Phase transformations and changes in properties of the steel during welding]. Moscow, Nauka Publ., 1972. 228 p. (Rus.)
Finkel V.M. Fizika razrushenija [Destruction Physics]. Moscow, Metallurgija Publ., 1970. 376 p.
Lisov V.S., Makarova T.A., Fedorov V.G. Structura i stoykost protiv obrazovanija holodnikh treshchyn metalla okoloshovnoy zony staly 38HS. [The structure and firmnees against of the cold crack formation of the metal heat affected zone steel 38HS]. Svarochnoe proizvodstvo – Welding production, 1982, no. 2, pp. 19-21. (Rus.)
Ivanova N.V., Dykun V.N., Vinokurov V.A. Hladostoykost metalla ZTW svarnykh sojedyneniy rezervuarnykh constructsiy [Cold resistance of HAZ metal of tank constructions welded joints]. Svarochnoe proizvodstvo – Welding production, 1985, no. 11, pp. 15-17. (Rus.)
Kalensky V.K., Chernyak J.P., Vasilyev V.G., Solomiychuk T.G. Vlijanije pogonnoy energiji na obrazovanije otkolov pry naplavke vysokouglerodystoy staly austenitnimy provolokamy [Effect of heat input on the formation of splits in high steel deposition austenitic wires]. Avtomaticheskaja svarka – Automatic welding, 2001, no. 11, pp. 11-14. (Rus.)
Steklov O.I., Alekseev A.V., Alexandrov O.A. Stoycost naplavlennogo sloja protyv otslaivanija v vodorodosoderzhashchykh sredakh [The deposited layer resistance against layer removing in hydrogen environments]. Svarochnoe proizvodstvo – Welding production, 1989, no. 12, pp. 8-10. (Rus.)
Suslova E.A., Ignatov V.A., Zubchenko A.S. Vlyjanije tekhnologycheskikh factorov na sklonnost k obrazovaniju treshchyn [Influence of technological factors on the crack susceptibility]. Svarochnoe proizvodstvo – Welding production, 1990, no. 5, pp. 35-36. (Rus.)
Gotalsky Yu.N., Snisar V.V., Novikova D.P. Sposoby suzhenija martensytnoy prosloykji v zonje splavlenija perlytnoy staly s austenytnim shwom [Martensitic layer contraction methods in pearlite steel fuson zone with austenitic weld]. Svarochnoe proizvodstvo – Welding production, 1981, no. 6, pp. 7-9. (Rus.)
Downloads
How to Cite
Issue
Section
License
The journal «Reporter of the Priazovskyi State Technical University. Section: Technical sciences» is published under the CC BY license (Attribution License).
This license allows for the distribution, editing, modification, and use of the work as a basis for derivative works, even for commercial purposes, provided that proper attribution is given. It is the most flexible of all available licenses and is recommended for maximum dissemination and use of non-restricted materials.
Authors who publish in this journal agree to the following terms:
1. Authors retain the copyright of their work and grant the journal the right of first publication under the terms of the Creative Commons Attribution License (CC BY). This license allows others to freely distribute the published work, provided that proper attribution is given to the original authors and the first publication of the work in this journal is acknowledged.
2. Authors are allowed to enter into separate, additional agreements for non-exclusive distribution of the work in the same form as published in this journal (e.g., depositing it in an institutional repository or including it in a monograph), provided that a reference to the first publication in this journal is maintained.