Investigation and analysis of the possibility of diffusionless phase transformations in the surface layer of a part under the action of grinding temperatures
DOI:
https://doi.org/10.15587/1729-4061.2018.140982Keywords:
austenite, martensite, γ-iron, α-iron, heating rate, transformation temperature, martensite range, surface layer, critical temperatureAbstract
The possibility of diffusionless phase transformations in the surface layer of the ground part under the influence of instantaneous grinding temperature is investigated and analyzed. This is important because the phase Feα-Feγ transformations that may occur when grinding parts lead to the appearance of so-called grinding burns, which 2-3 times reduce the reliability and durability of the part in the working mechanism. The mechanism of phase transformations, the critical temperature of these transformations and the associated processing modes that provide this temperature are determined. This allows a reasonable approach to the definition of grinding modes and, if necessary, the application of the cooling method. In addition, the problem of optimizing grinding regimes can be solved if the processing performance is taken as a target function, and grinding temperature as a limitation. With rapid surface heating of the hardened steel part by the grinding temperature above the Ac1 line, there is a reverse martensitic transformation Feα→Feγ. The martensite range during cooling Mn-Mk to a large extent covers negative temperatures. Therefore, austenite is partially fixed in the surface layer, forming a so-called quenching burn. Dependences for determining the formation temperature for steel of any chemical composition, give the possibility to maintain the value of grinding temperature below this level during grinding. The mechanism of diffusionless reverse martensitic transformation in the high-speed surface heating by cutting grains (instantaneous temperature) is considered. The heating rate and the effect of the pressure produced by the abrasive grain on the metal during the chip removal are experimentally determined. Thus, the possibility of diffusionless phase transformation is substantiated and the dependences for the calculation of austenite formation temperatures are given, which in turn provides the opportunity to calculate safe processing regimes
References
- Chumachenko, T. V. (2011). Tekhnologicheskoe obespechenie kachestva i proizvoditel'nosti obrabotki poverhnostey sheek valov rotorov gazovyh turbin, napylennyh mineralokeramikoy. Odessa, 163.
- Lebedev, V. G., Klimenko, N. N., Al'-Adzhelat, S. A. (2013). Mekhanizm obrazovaniya prizhogov pri shlifovanii detaley iz zakalennyh staley. Naukovi notatky, 40, 141–144.
- Lobodyuk, V. A., Estrin, E. I. (2009). Martensitnye prevrashcheniya. Moscow: Fizmalit, 352.
- Kremen', Z. I., Yur'ev, V. G., Baboshkin, A. F. (2015). Tekhnologiya shlifovaniya v mashinostroenii. Sankt-Peterburg Politekhnika, 424.
- Biront V. S. Teoriya termicheskoy obrabotki. Krasnoyarsk, 2007. 234 p.
- Vliyanie teploty, obrazuyushcheysya pri shlifovanii. Biblioteka tekhnicheskoy literatury. Available at: http://delta-grup.ru/bibliot/39/76.htm
- Lebedev, V., Klimenko, N., Uryadnikova, I., Chumachenko, T., Ovcharenko, A. (2017). Martensite transformations in the surface layer at grinding of parts of hardened steels. Eastern-European Journal of Enterprise Technologies, 3 (12 (87)), 56–63. doi: https://doi.org/10.15587/1729-4061.2017.103149
- Lebedev, V. G., Klimenko, N. N. (2015). Zakonomernosti obrazovaniya prizhogov otpuska pri shlifovanii podshipnikovyh staley. Perspektyvni tekhnolohiyi ta prylady, 6, 35–40.
- Fedotov, A. K. (2012). Fizicheskoe materialovedenie. Vol. 2. Fazovye prevrashcheniya v metallah i splavah. Minsk: Vysshaya shkola, 446.
- Aleksandrova, M. Yu., Dobrynin, S. A., Firsov, G. I. (2008). Modelirovanie temperaturnogo polya na poverhnosti detali pri naruzhnom bescentrovom shlifovanii. Vestnik nauchno-tekhnicheskogo razvitiya. Nacional'naya Tekhnologicheskaya Gruppa, 10 (14), 46–53.
- Kremen', Z., Yur'ev, V., Baboshkin, A. (2017). Tekhnologiya shlifovaniya v mashinostroenii. Litres, 425.
- Salov, P. M., Salova, D. P., Vinogradova, T. G., Saikin, S. S. (2016). Thermal phenomena during internal grinding with sliding feed. Vektor Nauki Tol’yattinskogo Gosudarstvennogo Universiteta, 1, 42–47. doi: https://doi.org/10.18323/2073-5073-2016-1-42-47
- Li, X., Ma, X., Subramanian, S. V., Shang, C., Misra, R. D. K. (2014). Influence of prior austenite grain size on martensite–austenite constituent and toughness in the heat affected zone of 700MPa high strength linepipe steel. Materials Science and Engineering: A, 616, 141–147. doi: https://doi.org/10.1016/j.msea.2014.07.100
- Rajasekhara, S., Ferreira, P. J. (2011). Martensite→austenite phase transformation kinetics in an ultrafine-grained metastable austenitic stainless steel. Acta Materialia, 59 (2), 738–748. doi: https://doi.org/10.1016/j.actamat.2010.10.012
- Kaluba, W., Kaluba, T., Zielinska-Lipiec, A. (2007). Morphological Evolutions in Steels during Continuous Rapid Heating. Materials Science Forum, 539-543, 4669–4674. doi: https://doi.org/10.4028/www.scientific.net/msf.539-543.4669
- Li, C. H., Ding, Y. C., Lu, B. H. (2008). Innovative Technology Investigation into Integrate the Surface Hardening Process with the Grinding Precision Finishing for CBN Grinding Crankshaft. 2008 4th International Conference on Wireless Communications, Networking and Mobile Computing. doi: https://doi.org/10.1109/wicom.2008.3039
- Xu, Y. (1993). The role of retained austenite and residual stresses in rolling contac. DigitalCommons@University of Nebraska – Lincoln. 1993. Available at: http://digitalcommons.unl.edu/dissertations/AAI9611077/
- Jin, S., Huang, D., Morris, J. W. Jr., Thomas, G. (2010). Use of the reverse martensitic transformation and precipitation to enhance the strength and stability of austenite. Lawrence Berkeley National Laboratory, 18.
- Golovin, I. S., Komissarov, A. A., Kustov, S. B., Maikranz-Valentin, M., Siemers, C. (2010). Phase impact of thermal cycling on reversibility and anelastic- transformations ity of martensitic transformation in Fe-22Mn-3Si alloy. Metallofizika i Noveishie Tekhnologii, 32 (2), 191–201.
- Analyse des évolutions structurales et du comportement mécanique d'un acier au chrome-nickel-molybdène à très bas carbone du type Z1CNDA 12-09-02, en fonction des traitements thermiques. Available at: https://www.theses.fr/1989PA112002
- Lebedev, V., Klimenko, N., Chumachenko, T., Uryadnikova, I., Ovcharenko, A. (2016). Definition of the amount of heat released during metal cutting by abrasive grain and the contact temperature of the ground surface. Eastern-European Journal of Enterprise Technologies, 5 (7 (83)), 43–50. doi: https://doi.org/10.15587/1729-4061.2016.81207
- Mirzoev, D. A., Mirzoev, A. A., Chirkov, P. V. (2016). Leave martensite in the input of rapid heating. Bulletin of SUSU. Series: Mathematics. Mechanics. Physics, 8 (1), 61–65.
- Gulyaev, A. P. (2011). Metallovedenie. Moscow, 643.
- Blank, V. D., Estrin, E. I. (2011). Fazovye prevrashcheniya v tverdyh telah pri vysokom davlenii. Moscow, 412.
- Kaufman, L., Cohen, M. (1958). Thermodynamics and kinetics of martensitic transformations. Progress in Metal Physics, 7, 165–246. doi: https://doi.org/10.1016/0502-8205(58)90005-4
- Tkachenko, I. F. (1997). Raschetnoe opredelenie temperatury ravnovesiya mezhdu austenitom i martensitom. Vestnik Priazovskogo gosudarstvennogo tekhnicheskogo universiteta. Seriya: Tekhnicheskie nauki, 3, 81–82.
- Metodika prigotovleniya mikroshlifa. Available at: https://infourok.ru/laboratornaya-rabota-metodika-prigotovleniya-mikroshlifa-852852.html
- Mikroskop MIM-7. Available at: http://mikroskop-1.ru/?name=Mikroskopy~MIM-7&ref
- Gorlach, V. V., Egorov, V. L., Ivanov, N. A. (2006). Obrabotka, predstavlenie, interpretaciya rezul'tatov izmereniy. Omsk: Izdatel'stvo SibADI, 85.
- Maslov, E. N. (1984). Teoriya shlifovaniya materialov. Moscow: Mashinostroenie, 320.
- Lyubov, B. Ya. (2013). Kineticheskaya teoriya fazovyh prevrashcheniy. Moscow: Metallurgiya, 375.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2018 Ala Bezpalova, Vladimir Lebedev, Natalia Klimenko, Tatiana Chumachenko, Inga Uryadnikova
This work is licensed under a Creative Commons Attribution 4.0 International License.
The consolidation and conditions for the transfer of copyright (identification of authorship) is carried out in the License Agreement. In particular, the authors reserve the right to the authorship of their manuscript and transfer the first publication of this work to the journal under the terms of the Creative Commons CC BY license. At the same time, they have the right to conclude on their own additional agreements concerning the non-exclusive distribution of the work in the form in which it was published by this journal, but provided that the link to the first publication of the article in this journal is preserved.
A license agreement is a document in which the author warrants that he/she owns all copyright for the work (manuscript, article, etc.).
The authors, signing the License Agreement with TECHNOLOGY CENTER PC, have all rights to the further use of their work, provided that they link to our edition in which the work was published.
According to the terms of the License Agreement, the Publisher TECHNOLOGY CENTER PC does not take away your copyrights and receives permission from the authors to use and dissemination of the publication through the world's scientific resources (own electronic resources, scientometric databases, repositories, libraries, etc.).
In the absence of a signed License Agreement or in the absence of this agreement of identifiers allowing to identify the identity of the author, the editors have no right to work with the manuscript.
It is important to remember that there is another type of agreement between authors and publishers – when copyright is transferred from the authors to the publisher. In this case, the authors lose ownership of their work and may not use it in any way.