Synthesis of high-temperature superconducting ceramics in the Bi(Pb)-Sr-Ca-Cu-O system based on amorphous precursors
DOI:
https://doi.org/10.15587/1729-4061.2022.262452Keywords:
superconductivity, microstructure, elemental composition, ceramics, morphology, diffractogram, amorphous phaseAbstract
The paper presents the results of the synthesis of bismuth superconducting ceramics with compositions Bi1.6Pb0.4Sr2Can-1CunOy (n=2, 3, 5) based on amorphous ceramics obtained by ultrafast melt quenching. In order to increase the rate of formation of superconducting compounds, effective devices have been developed for melting and hardening melts under the action of IR radiation. The sample holder was made of platinum. Melting and hardening were carried out in a continuous mode in an oxidizing environment in a flowing air atmosphere. The study of the elemental composition of the precursor samples established a slight deviation towards a decrease in the cationic composition of the precursors (Bi, Pb and Ca), relative to the stoichiometric composition. An increase in oxygen content by 12–15 % was also found. Synthesis of superconducting compounds was carried out in the temperature range of 843–850 °C, depending on the composition. The study found that in the sample Bi1.6Pb0.4Sr2Ca4Cu5Oy (2245) the superconducting high-temperature phase 2223 crystallizes. It was found that the formation of the superconducting phase 2223 in the Bi1.6Pb0.4Sr2Ca4Cu5Oy composition occurs in a lower and wider temperature range (843–848 °C) compared to the Bi1.6Pb0.4Sr2Ca2Cu3Oy (2223) composition. The complete formation of the superconducting high-temperature phase 2223 in a sample with the nominal composition Bi1.6Pb0.4Sr2Ca2Cu3Oy (2223) was carried out in a narrow temperature range of 849–850 °C, in a strict temperature regime with the participation of the liquid phase. An increase in the rate of formation of the superconducting compound 2223 in both studied compositions by 1.5–2.5 times was established, compared with the solid-phase method and other melt methods
Supporting Agency
- The work was supported by the grant of the Ministry of Education and Science of the Republic of Kazakhstan AP09260251.
References
- Yadav, S., Upadhyay, P., Awadhiya, B., Kondekar, P. N. (2022). Ferroelectric Negative-Capacitance-Assisted Phase-Transition Field-Effect Transistor. IEEE Transactions on Ultrasonics, Ferroelectrics, and Frequency Control, 69 (2), 863–869. doi: https://doi.org/10.1109/tuffc.2021.3130194
- Nogai, A. S., Nogai, A. A., Stefanovich, S. Y., Solikhodzha, Z. M., Uskenbaev, D. E. (2020). Dipole Ordering and the Ionic Conductivity in Na3Fe2(PO4)3-Type NASICON-Like Structures. Physics of the Solid State, 62 (8), 1370–1379. doi: https://doi.org/10.1134/s1063783420080259
- Deyneko, N., Zhuravel, A., Mikhailova, L., Naden, E., Onyshchenko, A., Savchenko, A. et. al. (2020). Devising a technique to improve the efficiency of CdS/CdTe/Cu/Au solar cells intended for use as a backup power source for the systems of safety and control of objects. Eastern-European Journal of Enterprise Technologies, 6 (5 (108)), 21–27. doi: https://doi.org/10.15587/1729-4061.2020.220489
- Gulamova, D. D., Uskenbaev, D. E., Chigvinadze, D. G., Magradze, O. V. (2008). Crystallization and synthesis of HTSC of compositions 2234, 2245 in the Bi-Pb-Sr-Ca-Cu-O system based on amorphous precursors obtained by solar radiation hardening. Applied Solar Energy, 44 (1), 42–45. doi: https://doi.org/10.3103/s0003701x08010131
- Kuznetsov, S. B. (1995). Combined system of levitation, propulsion and guidance for Maglev vehicles using high-temperature superconducting magnetic potential well. IEEE Transactions on Appiled Superconductivity, 5 (2), 614–617. doi: https://doi.org/10.1109/77.402625
- Sato, K., Hayashi, K., Ohmatsu, K., Fujikami, J., Saga, N., Shibata, T. et. al. (1997). HTS large scale application using BSCCO conductor. IEEE Transactions on Appiled Superconductivity, 7 (2), 345–350. doi: https://doi.org/10.1109/77.614500
- Larbalestier, D., Gurevich, A., Feldmann, D. M., Polyanskii, A. (2001). High-Tc superconducting materials for electric power applications. Nature, 414 (6861), 368–377. doi: https://doi.org/10.1038/35104654
- Keene, M. N., Goodyear, S. W., Satchell, J. S., Edwards, J. A., Chew, N. G., Humphreys, R. G. (1993). Thin film HTc SQUID construction and characterisation. IEEE Transactions on Applied Superconductivity, 3 (1), 2430–2433. doi: https://doi.org/10.1109/77.233946
- An, D. Y., Yuan, J., Kinev, N., Li, M. Y., Huang, Y., Ji, M. et. al. (2013). Terahertz emission and detection both based on high-Tc superconductors: Towards an integrated receiver. Applied Physics Letters, 102 (9), 092601. doi: https://doi.org/10.1063/1.4794072
- Fyk, O., Kucher, D., Kucher, L., Gonchar, R., Antonetsʹ, V., Fyk, M., Besedin, Y. (2018). Analysis of the technology to manufacture a high-temperature microstrip superconductive device for the electromagnetic protection of receivers. Eastern-European Journal of Enterprise Technologies, 5 (12 (95)), 38–47. doi: https://doi.org/10.15587/1729-4061.2018.144125
- Schulz, R. R., Chesca, B., Goetz, B., Schneider, C. W., Schmehl, A., Bielefeldt, H. et. al. (2000). Design and realization of an all d-wave dc π-superconducting quantum interference device. Applied Physics Letters, 76 (7), 912–914. doi: https://doi.org/10.1063/1.125627
- Devoret, M. H., Martinis, J. M. (2005). Implementing Qubits with Superconducting Integrated Circuits. Experimental Aspects of Quantum Computing, 163–203. doi: https://doi.org/10.1007/0-387-27732-3_12
- Jurbergs, D. C., Haupt, S. G., Lo, R.-K., Jones, C. T., Zhao, J., Mcdevitt, J. T. (1995). Electrochemical and optical devices based on molecule/high-Tc superconductor structures. Electrochimica Acta, 40 (10), 1319–1329. doi: https://doi.org/10.1016/0013-4686(95)00067-o
- Xiong, W., Kula, W., Sobolewski, R. (1994). Fabrication of High-T c Superconducting Electronic Devices Using the Laser-Writing Technique. Advances in Cryogenic Engineering Materials, 385–391. doi: https://doi.org/10.1007/978-1-4757-9053-5_50
- Palka, R. (2005). Modelling of high temperature superconductors and their practical applications. International Compumag Society Newsletter, 12 (3), 3–12. Available at: http://www.compumag.org/jsite/images/stories/newsletter/ICS-05-12-3-Palka.pdf
- Hull, J. R., Strasik, M. (2010). Concepts for using trapped-flux bulk high-temperature superconductor in motors and generators. Superconductor Science and Technology, 23 (12), 124005. doi: https://doi.org/10.1088/0953-2048/23/12/124005
- Eab, C.-H., Tang, I.-M. (1989). Upper limit for the Tc's of the “new” high Tc superconductors. Physics Letters A, 134 (4), 253–256. doi: https://doi.org/10.1016/0375-9601(89)90405-2
- Tret'yakov, Yu. D., Kazin, P. E. (1993). Novye problemy i resheniya v materialovedenii keramicheskikh sverkhprovodyaschikh kupratov. Neorganicheskie matererialy, 29 (12), 1571–1581.
- Chatterjee, S., Bhattacharya, S., Chaudhuri, B. K. (1998). Structural and transport properties of (Bi,Pb)4Sr3Ca3Cu4−mFemOx (m=0–0.06) glasses: Precursors for high Tc superconductors. The Journal of Chemical Physics, 108 (7), 2954–2961. doi: https://doi.org/10.1063/1.475682
- Aruchamy, A., Kim, S. J., Birnie, D. P., Uhlmann, D. R. (1993). Glass microstructure and initial crystallization of Pb0.32Bi1.68Sr1.75Ca2Cu3Ox. Journal of Non-Crystalline Solids, 160 (1-2), 60–67. doi: https://doi.org/10.1016/0022-3093(93)90284-5
- Coskun, A., Ozcelik, B., Kiymac, K. (2001). Physical Properties of Melt-Cast Annealed Bi1.6Pb0.4Sr2Ca3Cu4O12 Compound. Turkish Journal of Physics, 25, 473–479. Available at: https://journals.tubitak.gov.tr/cgi/viewcontent.cgi?article=1938&context=physics
- Gulamova, D. D., Bobokulov, S. K., Turdiev, Z. S., Bakhronov, K. N. (2018). High-Temperature Superconductors of the Bi1.7Pb0.3Sr2Ca(n– 1)CunOy (n = 2–20) Series Synthesized under the Influence of Concentrated Solar Energy. Applied Solar Energy, 54 (5), 358–360. doi: https://doi.org/10.3103/s0003701x18050067
- Gulamova, D. D., Uskenbaev, D. E., Fantozzi, G., Chigvinadze, J. G., Magradze, O. V. (2009). Phase composition and properties of superconducting ceramics based on Bi1.7Pb0.3Sr2Ca2Cu3O y precursors fabricated by melt quenching in a solar furnace. Technical Physics, 54 (6), 860–864. doi: https://doi.org/10.1134/s1063784209060140
- Gulamova, D. D., Uskenbaev, D. E. (2006). Effect of substrate composition and crystal structure on the BSCCO texture with the 2223 composition obtained under the action of solar radiation. Applied Solar Energy, 42 (4), 40–42.
- Uskenbayev, D. E., Nogay, A. S., Aynakulov, E. B. (2016). Properties of Bismuth-Based Superconductors Precursors obtained under the influence of the Radiant Flux. IOP Conference Series: Materials Science and Engineering, 110, 012030. doi: https://doi.org/10.1088/1757-899x/110/1/012030
- Maeda, H., Chen, W. P., Inaba, T., Sato, M., Watanabe, K., Motokawa, M. (2001). Texture development in Bi-based superconductors grown in high magnetic fields and its effect on transformation of Bi(Pb)2212 to Bi(Pb)2223. Physica C: Superconductivity, 354 (1-4), 338–341. doi: https://doi.org/10.1016/s0921-4534(01)00050-8
- Murashov, V. A., Frolov, A. M., Lebedev, A. V. (1988). Kationnoe zameschenie v vismutovykh sverkhprovodyaschikh kupritakh. I Vsesoyuz. sovesch. po VTSP. Tez. dokl. Vol. 3. Kharkiv, 116–118.
- Abe, Y. (1997). Superconducting Glass-Ceramics in Bi-Sr-Ca-Cu-O. World Scientific. doi: https://doi.org/10.1142/3537
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2022 Daniyar Uskenbaev, Kairatbek Zhetpisbayev, Adolf Nogai, Renat Beissenov, Ainur Zhetpisbayeva, Kymbat Baigisova, Yerkebulan Salmenov, Artur Nogai, Serua Tursyntay
![Creative Commons License](http://i.creativecommons.org/l/by/4.0/88x31.png)
This work is licensed under a Creative Commons Attribution 4.0 International License.
The consolidation and conditions for the transfer of copyright (identification of authorship) is carried out in the License Agreement. In particular, the authors reserve the right to the authorship of their manuscript and transfer the first publication of this work to the journal under the terms of the Creative Commons CC BY license. At the same time, they have the right to conclude on their own additional agreements concerning the non-exclusive distribution of the work in the form in which it was published by this journal, but provided that the link to the first publication of the article in this journal is preserved.
A license agreement is a document in which the author warrants that he/she owns all copyright for the work (manuscript, article, etc.).
The authors, signing the License Agreement with TECHNOLOGY CENTER PC, have all rights to the further use of their work, provided that they link to our edition in which the work was published.
According to the terms of the License Agreement, the Publisher TECHNOLOGY CENTER PC does not take away your copyrights and receives permission from the authors to use and dissemination of the publication through the world's scientific resources (own electronic resources, scientometric databases, repositories, libraries, etc.).
In the absence of a signed License Agreement or in the absence of this agreement of identifiers allowing to identify the identity of the author, the editors have no right to work with the manuscript.
It is important to remember that there is another type of agreement between authors and publishers – when copyright is transferred from the authors to the publisher. In this case, the authors lose ownership of their work and may not use it in any way.